Entisar Mohson Hameed
Abstract
This paper is amid to study the effect of immersion solusion type on corrosion resistance of austenitic stainless steel AISI 304L . The process welding carried out on sheet metal by ...
Read More ...
This paper is amid to study the effect of immersion solusion type on corrosion resistance of austenitic stainless steel AISI 304L . The process welding carried out on sheet metal by using four types of electrodes (E308L,E309L,E312,E347) to obtain butt joint welding under constant conditions polarity(DCSP) , voltage(30)v, current (120)A . Welding speed (100) mm/min and two weld passes by using electrode of diameter 3 mm. Many specimens for corrosion test were manufactured in (20*20*8) mm from welding joint stainless steel. Corrosion test was implemented by using weight loss, specimens were immersed in two solution (1% H2SO4) Sulphric Acid and (3.5%Nacl) sea water for (1-30 ) days and corrosion rate was measured. The results show that sulphric acid was more effected on stainless steel.